Qatar Q1018N
The Qatar Q1018N is a linear low-density polyethylene (LLDPE) product manufactured by Qatar Olefins Company.
The melt flow rate was 1g/10min and the density was 0.918g/cm3.
Product features: It has high impact resistance and high strength, and also has good thermal stability, weather resistance and aging resistance.
Application fields: Through injection molding and extrusion molding processing methods, we produce agricultural films, multi-layer co-extruded films, industrial films for building materials, daily storage containers, and food films with specific performance requirements for the food industry.
|
Physical property |
Test condition |
Attribute value |
Unit |
Test method |
|
Melt index |
190℃/2.16 kg |
1.0 |
g/10 min |
ASTM D1238 |
|
Density |
0.918 |
g/cm³ |
ASTM D792 |
|
Mechanical behavior |
Test condition |
Attribute value |
Unit |
Test method |
|
Tensile yield strength |
Vertical: 40 μm, blown film |
11.0 |
MPa |
ASTM D882 |
|
Tensile yield strength |
Horizontal: 40 μm, blown film |
11.0 |
MPa |
ASTM D882 |
|
Tensile fracture strength |
Vertical: 40 μm, blown film |
38.0 |
MPa |
ASTM D882 |
|
Tensile fracture strength |
Horizontal: 40 μm, blown film |
33.0 |
MPa |
ASTM D882 |
|
Drop hammer impact |
40 μm, blow molding thin film |
150 |
g |
ASTM D1709 |
|
Secant modulus |
1% tangent, vertical To: 40μm, blown film |
215 |
MPa |
ASTM D882 |
|
Secant modulus |
1% tangent, horizontal To: 40 μm, blown film |
245 |
MPa |
ASTM D882 |
|
Elongation at break |
Horizontal: 40 μm, blown film |
850 |
% |
ASTM D882 |
|
Elongation at break |
Vertical: 40 μm, blown film |
800 |
% |
ASTM D882 |
|
Elmandov Tearing strength |
Horizontal: 40 μm, blown film |
480 |
g |
ASTM D1922 |
|
Elmandov Tearing strength |
Vertical: 40 μm, blown film |
280 |
g |
ASTM D1922 |
|
Hot property |
Test condition |
Attribute value |
unit |
Test method |
|
Vickers softening point |
100 |
℃ |
ASTM D1525 |
|
|
Crystallization point |
122 |
℃ |
internalist methodology |
|
Optical performance |
Test condition |
Attribute value |
Unit |
Test method |
|
Fog level |
40.0 μm, blow plastic film |
11 |
% |
ASTM D1003 |
|
Glossiness |
45°,40.0 μm, blown film |
60 |
not have |
ASTM D2457 |
|
Squeeze out |
Attribute value |
Unit |
|
Temperature in Zone 1 of the barrel |
180 to 220 |
℃ |
|
Temperature in Zone 2 of the barrel |
180 to 220 |
℃ |
|
Temperature in Zone 3 of the barrel |
180 to 220 |
℃ |
|
Temperature in Zone 4 of the barrel |
180 to 220 |
℃ |
|
Temperature in Zone 5 of the barrel |
180 to 220 |
℃ |
|
Melting temperature |
200 |
℃ |
Hot Tags: LLDPE for film blowing, China LLDPE for film blowing manufacturers, factory, High Light Transmittance LLDPE, LLDPE for Membranes, High Transparency LLDPE for Packaging, LLDPE for Commodity Packaging, LLDPE with Excellent Tensile Properties, LLDPE Is Used for High impact Packaging Materials