Technical Specifications: Features high tensile strength (≥28MPa in longitudinal direction and ≥25MPa in transverse direction per ISO 527-3), with excellent puncture resistance (≥850g impact per ASTM D1709). Ideal for blow molding processes, it ensures bubble stability with thickness deviation ≤5% and a low heat seal initiation temperature of 110°C, making it suitable for high-speed packaging lines. The material exhibits haze ≤10% and gloss ≥85% (per ASTM D1003), delivering outstanding optical performance.
|
mechanical behavior |
test condition |
attribute value |
unit |
test method |
|
tensile yield strength |
Horizontal: 50 μm |
11 |
MPa |
ISO 527-3 |
|
tensile yield strength |
Vertical: 50μm |
11 |
MPa |
ISO 527-3 |
|
modulus in tension |
Vertical: 50μm |
160 |
MPa |
ISO 527-3 |
|
modulus in tension |
Horizontal: 50μm |
180 |
MPa |
ISO 527-3 |
|
tensile fracture strength |
Horizontal: 50μm |
30 |
MPa |
ISO 527-3 |
|
tensile fracture strength |
Vertical: 50 μm |
37 |
MPa |
ISO 527-3 |
|
elongation at break |
Vertical: 50 μm |
700 |
% |
ISO 527-3 |
|
elongation at break |
Horizontal: 50 μm |
850 |
% |
ISO 527-3 |
Hot Tags: excellent puncture resistance for blow molding processes, China excellent puncture resistance for blow molding processes manufacturers, factory, Excellent Processing Performance LLDPE, High Impact LLDPE, High transparency LLDPE, High transparency Polyethylene Insulation, LLDPE for Membranes, Low Haze LLDPE